INCOFLUXR NT110 埋弧焊劑
INCOFLUX NT110 埋弧焊劑設計與MONEL 60／67焊絲匹配使用，MONEL 60焊絲是一種含銅30％含鎳70％的合金，而MONEL 67焊絲含銅70％含鎳30％。這種焊劑的典型應用是與MONEL 60匹配，用于MONEL 400合金自身之間及其與鐵素體金屬材料之間的開坡口焊接。這種焊劑的一個主要應用是與MONEL 60填充金屬相匹配，在碳鋼表面堆焊形成耐蝕保護層。這種焊劑還可以與MONEL 67填充金屬匹配應用于MONEL 450或其它銅-鎳合金（銅鎳比例為：90／10、80／20及70／30）的焊接。如果在鋼的表面進行堆焊，需要用INCONEL 61或MONEL 60填充金屬打底作過渡層。
|
焊接參數：開坡口焊或堆焊：應用DCEP電流方式和窄焊道 |
||||||
|
焊絲直徑 |
電流／安培 |
電壓／伏特 |
焊接速度 |
電極干伸長 |
焊劑層厚度 |
|
|
0.062 in 1.6 mm |
260-280 |
30-33 |
8-11 in/min 200-280mm/min |
7/8-1 in 22-25 mm |
1/2-1 in 13-25 mm |
|
|
0.093 in 2.4mm |
300-350 |
32-35 |
8-11 in/min 200-280mm/min |
7/8-1 in 22-25 mm |
3/4-5/4 in 19-32 mm |
|
|
電極擺動堆焊：應用DCEN電流方式，當焊絲直徑為0.062 in時，擺動頻率為50-70周／分；當焊絲直徑為0.093 in時，擺動頻率為35-50周／分 |
||||||
|
0.062 in 1.6 mm |
260-280 |
32-35 |
4 in/min 100mm/min |
7/8-1 in 22-25 mm |
1/2-1 in 13-25 mm |
|
|
0.093 in 2.4mm |
300-400 |
34-37 |
4 in/min 100mm/min |
7/8-1 in 22-25 mm |
3/4-5/4 in 19-32 mm |
|
儲藏和干燥條件
焊劑密封在未開啟的容器中可以無限期保存。如果焊劑暴露于潮濕環境中，可以在500oF保溫烘干2小時或600oF保溫烘干1小時后使用。
|
焊劑顆粒尺寸 泰勒制網目：10×100目
|
|
包裝
桶蓋上帶有橡膠密封墊圈的60磅聚乙烯桶密封包裝
|
The INCOFLUX NT110 submerged arc welding is designed to match the MONEL 60/67 welding wire, and the MONEL 60 welding wire is an alloy with 30 % copper and 70 % of copper content, while MONEL 67 electrode contains 70 % nickel and 30 %. The typical application of this flux is to match the MONEL 60 for the MONEL 400 alloy itself and its weld with the open groove between the ferrite metal materials. One of the main applications of this flux is to match with the MONEL 60 filler metal, which is surfacing on the surface of carbon steel to form an anticorrosive coating. This flux can also be used to weld MONEL 67 with metal matching for MONEL 450 or other copper-nickel alloys (90/10, 80/20 and 70/30 for copper and nickel). If the surface of the steel is surfacing, the metal bottom will need to be filled with INCONEL 61 or MONEL 60.
Welding parameters: open groove welding or surfacing: apply DCEP current and narrow weld path
Electrode dry extension flux layer thickness of wire diameter current/ampere voltage/v welding speed electrode
0.062 in
1.6 mm 260-280 30-33 8-11 in/min
In 200-280 - mm/min 7/8-1
1/2-1 in 22 to 25 mm
13 to 25 mm
0.093 in
2.4mm 300-350 32-35 8-11 in/min
In 200-280 - mm/min 7/8-1
22-25 mm 3/4-5/4 in
19 to 32 mm
Electrode swing surfacing welding: the use of DCEN current mode, when the wire diameter is 0.062 in, the oscillation frequency is 50-70 weeks/min; When the wire diameter is 0.093 in, the oscillation frequency is 35-50 weeks/min
0.062 in
1.6 mm 260-280 32-35 4 in/min
100 mm/min in 7/8-1
1/2-1 in 22 to 25 mm
13 to 25 mm
0.093 in
2.4mm 300-400 34-37 4 in/min
100 mm/min in 7/8-1
22-25 mm 3/4-5/4 in
19 to 32 mm
Storage and drying conditions
The flux seals can be kept indefinitely in unopened containers. If the solder is exposed to wet conditions, it can be used after an hour of thermal insulation drying for 2 hours or 600oF.
Flux particle size
Taylor's mesh: 10 times 100
packaging
The barrel cover is covered with a 60 - pound polyethylene barrel sealed with rubber gasket